BOPP Double Sides Hazy Film for Capacitor

• Type: Film
• Material: Plastic
• for Metallization: MP-1
• Model NO.: RP, RRP
• High Temperature Resistance: MP-H
• Transport Package: Pallet
• Trademark: FSPG Products
• Origin: Foshan, Guangdong, China
• HS Code: 3920209090
• Production Capacity: 10000mt/Y

Product Description

Metallizable base film: The product has good thickness uniformity, stable electrical properties, good winding property, good metal evaporation ability, and the main thickness specification of the product is 2.4micro to 12 micro.
Product application scope: metallized base film and metallized coating are mainly used in: new energy industry: photovoltaic inverter, wind power converter, etc.; power industry: large high frequency switching power supply, UPS, emergency power EPS, intermediate frequency power supply, DC stabilized power supply, electroplating power supply, chemical power supply, etc.; electric locomotive industry: locomotive traction converter, Metro, high-speed rail, light rail, etc , tram; power quality industry: dynamic synchronous var compensator SVG, active power filter APF, etc.; energy saving industry: high voltage inverter, etc.; home appliance industry: filter protection, etc.



BOPP metalized base film for capacitor

Items		Test Methods	Units	Typical Value
Thickness		GB 6672	μm	7
Ave. Variation of Thickness		GB/T13541	%	+0.2
Tensile strength       (MD/TD)		GB 13022	MPa	160/280
Elongation at Break   (MD/TD)		GB 13022	%	145/50
Heat Shrinkage       (MD/TD)	MP-1	GB 12026	%	3.5/0.5
	MP-H			3.0/0.1
Density		GB 1033	g/cm^3	0.91
Surface  Roughness(in/out)		GB/T13541	μm	0.08/0.08
Wet Tension        (Treated Side)		GB/T 14216	mN/m	40
Dielectric Strength(Ave/Min)DC		GB/T13541	V/μm	496/406
Dielectric Constant		GB/T 13541	--	2.2
Dielectric Consumed Angle tangent		GB/T 13541	--	2.0×10^-4
Volume Resistivity		GB/T 13541	Ω·m	1.9×10^15

BOPP hazy film for capacitor

Items			Units	Typical Value
Thickness			μm	15
Ave. Variation of Thickness			%	+0.2
Tensile strength        (MD/TD)			MPa	155/258
Elongation at Break    (MD/TD)			%	125/49
Heat Shrinkage        (MD/TD)			%	3.0/0.3
Voidage	Average		%	10.6
	Max.			11.1
	Min			10.1
Dielectric Strength  DC	Average		V/μm	550
	Min.			515
Electric strength (d.c. test)	Central value		V/μm	356
	Not more than 1 of 21 results shall be below			305
Dielectric Constant			--	2.2
Dissipation factor			--	2.0×10^-4
Volume Resistivity			Ω·m	3.2×10^15
Surface Roughness(In/Out)		Ra	μm	0.42/0.40

Items			Units	Typical Value
Thickness			μm	15
Ave. Variation of Thickness			%	+0.2
Tensile strength        (MD/TD)			MPa	155/258
Elongation at Break    (MD/TD)			%	125/49
Heat Shrinkage        (MD/TD)			%	3.0/0.3
Voidage	Average		%	10.6
	Max.			11.1
	Min			10.1
Dielectric Strength  DC	Average		V/μm	550
	Min.			515
Electric strength (d.c. test)	Central value		V/μm	356
	Not more than 1 of 21 results shall be below			305
Dielectric Constant			--	2.2
Dissipation factor			--	2.0×10^-4
Volume Resistivity			Ω·m	3.2×10^15
Surface Roughness(In/Out)		Ra	μm	0.42/0.40